Comfil® TFC

By FILLAUER

Description

• Combines the high strength of carbon composite with the molding properties of a thermoplastic
• Available in two forms: U-D Form (with 90% strength unidirectionally) and 3-D Form (same strength bidirectionally)
• Can be heated in oven or heat gun
• Easily cut with scissors
• Easily formed to accommodate ankle or knee joints
• Components: Carbon fibre filament yarn (weight 30–80%) and thermoplastic filaments (weight 20–70%)
• Carbon filament yarn composed of carbon fiber on basis polyacrylonitrile >95% and alkylimidazolinium ethosulphat <5%

Additional Information

Width 600mm (23 5/8")
Unit Sheet
Heating Time 2-3 minutes
Note 1 After pieces have been tacked together place in heated oven at 220°C (428°F) for approximately 45 minutes to consolidate
Colour Black
Length 100cm (39 3/8")
Heating Temperature 100°C (212°F)

Comfil<sup>®</sup> TFC

More Views

Sku Thickness Style
DF-700010101 1.6mm (1/16”) UD Form (100% Carbon fibre)
DF-700010103 2.55mm (3/32") UD Form (70% Glass fibre/30% Carbon fibre)
DF-700010121 0.75mm (1/32") 3D Form (100% Glass fibre)
DF-700010122 1.5mm (1/16”) 3D Form (100% Glass fibre)
DF-700010123 1.5mm (1/16”) 3D Form (50% Glass fibre/50% Carbon fibre)
DF-700010124 0.7mm (1/32") 3D Form (100% Carbon fibre)
DF-700010125 2.1mm (3/32") 3D Form (50% Glass fibre/50% Carbon fibre)
DF-700010126 0.7mm (1/32") UD Form (100% Carbon fibre)
DF-700010127 0.5mm (1/32") 3D Form (100% Carbon fibre)